Activated koalin powder compound for mixing with cement and method of preparing the same

ABSTRACT

The activated kaolin powder compound is prepared from naturally-existing kaolin (hereinafter &#34;natural kaolin&#34;). The activated kaolin powder compound is prepared by heating natural kaolin to 480° C. within at most one hour, calcinating the heated natural kaolin at high temperature by heating in the range of 800~950° C. over at least 15 minutes, quenching the calcinated kaolin with water or air, and pulverizing the quenched activated kaolin to give powder having particle sizes of 2 mum or less, wherein the natural kaolin is primarily composed of halloysite (Al2O3.2SiO2.4H2O). The activated kaolin powder compound is employed in an amount of about 5 to 15% by weight of cement for preparing mortar or cement. The cement composition containing the activated kaolin powder compound can provide a mortar or concrete having excellent properties in compressive strength, flexural strength and water permeability.

This application is a continuation-in-part-of application Ser. No. 08/925,951 filed Sep. 8, 1997 now U.S. Pat. No. 5,976,241.

FIELD OF THE INVENTION

The present invention relates to an activated kaolin powder compound for mixing with cement. More particularly, this invention relates to an activated kaolin powder compound for mixing with cement so as to provide mortar or concrete having good physical properties in strength, water permeability, etc. This invention also relates to a method of preparing the activated kaolin powder compound.

BACKGROUND OF THE INVENTION

In general, mortar or concrete using cement requires excellent strength and water permeability. A number of various researches have been carried out to prepare mortar or concrete having excellent physical properties in strength, water permeability, etc. For this purpose, many researches have been continued both in the field of cement and in the field of other mixing components used with the cement. As one of the mixing components, silica fume has been developed to prepare mortar or concrete having excellent physical properties in strength, water permeability, etc. when it is used with cement. However, the silica fume is very expensive and cannot be widely used at present.

Accordingly, the present inventors have developed an activated kaolin powder compound for using with cement so that the mortar or concrete prepared from the composition of cement and the activated kaolin powder shows good properties in strength and water permeability. The kaolin is naturally buried under the ground and can be obtained in a much lower cost than the silica fume.

OBJECTS OF THE INVENTION

An object of the present invention is to provide an activated kaolin powder compound which can be used with cement.

Another object of the invention is to provide an activated kaolin powder compound to prepare mortar or concrete having good properties in strength and water permeability, when the activated kaolin powder compound is together used with cement.

A further object of the invention is to provide a method of preparing an activated kaolin powder compound from a naturally-existing kaolin.

A still further object of the invention is to provide mortar or concrete having excellent strength and water permeability, which can be prepared by using an activated kaolin powder compound of this invention in a lower cost.

The foregoing and other objects of the present invention will be achieved in the following description.

SUMMARY OF THE INVENTION

The activated kaolin powder compound is prepared from naturally-existing kaolin (hereinafter “natural kaolin”). The activated kaolin powder compound is prepared by heating natural kaolin to 480° C. for a time period up to one hour, calcinating the heated natural kaolin at 800˜950° C. over at least 15 minutes, quenching the calcinated kaolin with water or air, and pulverizing the quenched activated kaolin to give powder having particle sizes 2 μm or less.

The activated kaolin powder compound is employed in an amount of about 5 to 15% by weight of cement for preparing mortar or cement.

The cement composition containing the activated kaolin powder compound can provide a mortar or concrete having excellent properties in compressive strength, flexural strength and water permeability.

BRIEF DESCRIPTION OF THE DRAWINGS

The present invention will be more fully understood by reference to the following detailed description of the preferred embodiment of the present invention when read in conjunction with the accompanying drawings.

FIG. 1 is a schematic graph showing the relationship of temperature with heating and calcinating time in the process of preparing an activated kaolin powder compound according to the present invention;

FIG. 2 is a cross-sectional view of a specimen of mortar for testing water permeability thereof, which is prepared in accordance with the present invention;

FIG. 3 is a graph showing an X-ray diffraction pattern of an unactivated kaolin powder (natural kaolin powder);

FIG. 4 is a graph showing an X-ray diffraction pattern of an activated kaolin powder according to the present invention;

FIG. 5 is a graph showing an X-ray diffraction pattern of a specimen which is prepared by mixing an unactivated kaolin powder with a lime; and

FIG. 6 is a graph showing an X-ray diffraction pattern of a specimen which is prepared by mixing an activated kaolin powder with a lime according to the present invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

The present invention utilizes natural kaolin which is buried under the ground in an tremendous amount. The natural kaolin is activated for use mixing with cement in this invention. The natural kaolin has been used for manufacturing pottery, porcelain, china, etc. In this invention, an activated kaolin powder has been developed from the natural kaolin, which is capable of being used as one of composite materials for mortar or concrete. The activated kaolin powder is prepared by heating natural kaolin to a certain temperature, calcinating the heated kaolin at high temperature, quenching the calcinated kaolin with water or air, and pulverizing the quenched activated kaolin in a form of powder.

Generally, activation of a mineral compound means a state wherein a large amount of crystallization energy is reserved in the molecular structure of the mineral compound when energy is applied to the mineral compound and then the mineral material is quenched, and wherein the mineral compound is in a free state having a strong chemical bonding ability due to the reserved crystallization energy when an external force is applied to the mineral compound.

When the natural kaolin is calcinated at high temperature and then quenched, the kaolin reserves a large amount of crystallization energy in the molecular structure and has a latent hydraulicity, because the kaolin molecules are in a free state. In other words, although the activated kaolin has a high reaction activity and does not cause a hydration when the kaolin contacts with water, the kaolin shows a significant water-setting under a certain circumstance, for instance, in an alkali state. Such water-setting is called as “latent hydraulicity”. The present invention is to provide a natural kaolin with the latent hydraulicity by activation, and to cause a mechanism for hydration and pozzolan reaction of the activated kaolin under a certain circumstance such as in mortar or in concrete.

The reactions intended to derive in the present invention are pozzolan reaction and straetlingite reaction, and the pozzolan reaction shown in the following reaction formula (I) is that a silica and Ca(OH)₂ are reacted each other, and the straetlingite reaction shown in the following formula (II) is that a silica, a alumina and Ca(OH)₂ are reacted each other.

 3Ca(OH)₂+2SiO₂=3CaO.2SiO₂.3H₂O  (I)

2Ca(OH)₂+Al₂O₃+SiO₂+6H₂O→2CaO.Al₂O₃.SiO₂.8H₂O  (II)

The activated kaolin according to the present invention and Ca(OH)₂ from cement cause a pozzolan reaction, and the mortar or concrete using the activated kaolin has excellent strength and water permeability due to the latent hydraulicity.

A bleeding or segregation phenomenon can be improved when a fine particle component is added to a mortar or concrete, which is called as “stabilizing effect”. In this invention, the activated kaolin powder causes the stabilizing effect. When the activated kaolin powder is added to a mortar or concrete, the bleeding or segregation phenomenon of the composition is reduced. Thus, the activated kaolin powder of this invention can cause an excellent stabilizing effect when the activated kaolin powder is together used with mortar or cement. This is believed because the activated kaolin powder fills the porosities of cement particles or reduces the porosity sizes, and because the activated kaolin powder increases the surface of cement paste and aggregate thereby increasing the bonding force of mortar or cement.

The activated kaolin powder compound is prepared from natural kaolin. The activated kaolin powder compound is prepared by heating natural kaolin to 480° C. (for a time period up to one hour, calcinating the heated natural kaolin at 800˜950° C. over at least 15 minutes, quenching the calcinated kaolin with water or air, and pulverizing the quenched activated kaolin to give powder having particle sizes of 2 μm or less.

A kaolin used in the present invention is primarily composed of halloysite(Al₂O₃.2SiO₂.4H₂O), and a composition thereof is Al₂O₃ of 36˜39%, SiO₂ of 45˜47% and CaO of 1˜2%, and has Al₂O₃/2SiO₂=0.76˜0.87. The kaolin without any treatment can be used in the present invention. A method of pulverizing the quenched activated kaolin comprises crushing by Crusher, and pulverizing by Air Jet Mill. The maximum particle size is 2 μm, and the average particle size is 0.1˜1.0 μm.

FIG. 1 is a schematic graph showing the relationship of temperature with heating and calcinating time in the process of preparing an activated kaolin powder compound according to the present invention.

As shown in FIG. 1, the natural kaolin which is dried at ambient temperature is heated to 480° C. It is preferable to heat the natural kaolin for a time period up to one hour in aspect of heat efficiency and energy consumption.

The heated natural kaolin is calcinated in the range of 800˜950° C. In this calcinating step, it is preferable to calcinate the heated kaolin over at least 15 minutes. For excellent physical properties of the activated kaolin powder compound, the calcinating step should be conducted for more than 15 minutes in consideration of the heat efficiency and amount of energy used. In this calcinating step, the temperature should be lower than 950° C., because the physical properties can be adversely affected at the higher temperature than 950° C. The starting temperature for activation of kaolin is in the range of 450˜500° C., and the terminating temperature for that is 980° C. The optimum temperature to improve the compressive strength is in the range of 800˜950° C.

The calcinated kaolin is quenched with water or air. A water-cooling method is more effective in cost than an air-cooling method. The air-cooling method is that the calcinated kaolin is quenched by using an air spray in the range of 20˜60° C., and the water-cooling method is that the calcinated kaolin is immersed in water ranging from 15 to 40° C. Through the quenching step, the kaolin is in an activation state which reserves crystallization energy therein.

The quenched kaolin is pulverized in a form of powder to give particle sizes of 2 μm or less. Kaolin particles having about 1 μm are preferably used. The pulverized kaolin powder has a specific gravity of 1.5 to 3.0.

The activated kaolin powder compound is employed in an amount of about 5 to 15% by weight of cement for preparing mortar or cement. It is preferable to employ the activated kaolin powder compound in an amount of about 10% by weight of the cement.

The activated kaolin powder compound is used for preparing mortar or concrete having excellent strength and water permeability, and being manufactured in an economical cost.

The invention may be better understood by reference to the following examples which are intended for purpose of illustration and are not to be construed as in any way limiting the scope of the present invention, which is defined in the claims appended.

EXAMPLE

Preparation of Specimens of Mortar

The activated kaolin powder, cement, sands and a superplasticizer were mixed to give mortar. The composition of mortar are described in the following Example and Comparative Examples. The cement has a specific surface of 3200 and a specific gravity of 3.28. The sands have a specific gravity of 2.61 and fine modulus of 2.71. The superplasticizer is a naphthalene compound having a specific gravity of 1.25.

Optimum Temperature for Activation of Kaolin

A specimen of mortar was prepared by mixing 450 g of cement, 50 g of activated kaolin, 1,500 g of sands, and 250 g of water. The calcination temperature for activation of kaolin was set up as room temperature, 200° C., 400° C., 600° C., 800° C., 1000° C., and 1200° C.

The activation of kaolin was started from 600° C. and terminated over 1000° C. It was found that the activation was started in the range of 400˜600° C., and was terminated in the range of 800˜1000° C. The results were shown in Table 1.

TABLE 1 calcination compressive specimen temperature(° C.) strength(kgf/cm²) 1 room temperature 186 2 200 204 3 400 175 4 600 373 5 800 431 6 1000 181 7 1200 218

To obtain the optimum temperature for activation of kaolin, a second experiment was carried out on the basis of the above results.

A kaolin was calcinated at 400° C., 450° C., 500° C., 550° C. and 600° C. The compressive strength of the specimen of mortar was not increased in the range of 400 and 450° C., and considerably increased at 500° C. It was found that the starting temperature for activation of kaolin is about 480° C. The results were shown in Table 2.

TABLE 2 calcination compressive specimen temperature(° C.) strength(kgf/cm²) 1 400 175 2 450 193 3 500 361 4 550 350 5 600 373

To obtain the optimum temperature for activation of kaolin, a kaolin was calcinated at 800° C., 850° C., 900° C., 950° C. and 1000° C. The compressive strength of the specimens of mortar was increased until 950° C., and considerably decreased over 1000° C. It was found that the terminated activation temperature of kaolin was about 980° C. The results were shown in Table 3.

Accordingly, it was found that the optimum temperature for activation of kaolin was in the range of 800˜950° C.

TABLE 3 calcination compressive specimen temperature(° C.) strength(kgf/cm²) 1 800 431 2 850 415 3 900 437 4 950 451 5 1000 181

Optimum Time for Activation of Kaolin

The specimens of mortar were prepared in the same manner as above Example, and the calcination temperature was fixed at 950° C., and the calcination time was set up as 40, 60, 80 and 100 minutes. As a result of testing the compressive strength of specimens, there were no big differences according to the calcination time. The results were shown in Table 4.

TABLE 4 calcination calcination compressive specimen temperature(° C.) time(minute) strength (kgf/cm²) 1 950 40 441 2 950 60 449 3 950 80 461 4 950 100 458

To obtain the optimum time for calcination of kaolin, a second experiment was carried out on the basis of the above results.

The calcination temperature was fixed at 950° C., and the calcination time was set up as 5, 10, 15, 20, 25, 30, 35 and 40 minutes. As a result of testing the compressive strength of specimens, there were no big differences after 15 minutes. The results were shown in Table 5. In consideration of the saving energy, it was found that the optimum calcination time for activation of kaolin was over at least 15 minutes.

TABLE 5 calcination calcination compressive specimen temperature(° C.) time(minute) strength(kgf/cm²) 1 950 5 310 2 950 10 369 3 950 15 415 4 950 20 420 5 950 25 435 6 950 30 438 7 950 35 440 8 950 40 442

Preparation of Activated Kaolin Powder

Ambient temperature dried natural kaolin from Sanchung-san, Kyungnam, Korea of 500 g was heated to 480° C. in a furnace for 40 minutes. The heated kaolin was calcinated at 950° C. for 90 minutes. The calcinated kaolin was quenched with water to prepare an activated kaolin compound. The activated kaolin compound was pulverized with a pulverizer. The activated kaolin powder having an average particle size of 1.2 μm and a specific gravity of 2.55 was obtained.

Analysis of Activated Kaolin and Natural Kaolin

The reaction tests of the kaolin with an alkali solution and X-ray diffraction analysis were carried out for the activated kaolin above and natural kaolin.

(1) Reaction Tests of the Kaolin With Ca(OH)₂ Solution and Phenolphthalein Solution

Activated kaolin was added to a saturated solution of Ca(OH)₂ and tested with an indicating agent of phenolphthalein solution. Activated kaolin reacted with Ca(OH)₂. As Ca(OH)₂ did not exist in the solution any more, the solution by reaction of phenolphthalein solution appeared white.

Unactivated kaolin was added to a saturated solution of Ca(OH)₂ and tested with an indicating agent of phenolphthalein solution. Unactivated kaolin did not react with Ca(OH)₂. As Ca(OH)₂ existed in the solution, the solution by reaction of phenolphthalein solution appeared red.

From these reaction tests, it is believed that the kaolin according to the present invention was activated.

(2) X-ray Diffraction Analysis X-ray diffraction analysis was conducted for the unactivated (natural) kaolin powder and the activated kaolin powder according to the present invention. The results were shown in FIG. 3 and FIG. 4.

From the X-ray diffraction patterns, it was found that there was no halloysite in the activated halloysite, while a lot of halloysite was exist in the unactivated kaolin. Accordingly, the halloysite in a state of crystalline became in a state of noncrystalline which has a reactivity.

Also, in order to confirm whether the activated kaolin has a reactivity, the kaolin and lime were mixed with the ratio of 2.5 to 1, and the structural change thereof was examined.

As shown in FIG. 5, the unactivated kaolin was in a state of halloysite, and the kaolin and lime were not reacted because the kaolin did not have reactivity, therefore the lime was transferred to calcium carbonate.

On the other hand, as shown in FIG. 6, the activated kaolin was in a free state of noncrystalline which has a reactivity. Therefore, the pozzolan reaction was carried out by reacting SiO₂ with Ca(OH)₂, and the straetlingite reaction was carried out by reacting Al₂O₃ with Ca(OH)₂. From those reactions, the compressive strength of mortar could be improved.

(I) Pozzolan reaction:

3Ca(OH)₂+2SiO₂+3CaO.2SiO₂.3H₂O

(II) Straetlingite reaction:

2Ca(OH)₂+Al₂O₃+SiO₂+6H₂O→2CaO.Al₂O₃.SiO₂.8H₂O

Example 1

Cement of 450 g, activated kaolin of 50 g, sands of 1,500 g, water of 250 g and superplasticizer of 5 g were mixed together. Specimens of mortar of 40×40×160 mm were prepared from the mixture. The specimens were wet-cured in a 3-in-1 mold for 24 hours, and water-cured for 28 days. Three specimens (Specimens I, II and III) were prepared.

Comparative Example 1

A conventional mortar was prepared. Cement of 500 g, sands of 1,500 g, water of 250 g and superplasticizer of 5 g were mixed together. Specimens of mortar of 40×40×160 mm were prepared from the mixture. The specimens were wet-cured in a 3-in-1 mold for 24 hours, and water-cured for 28 days. Three specimens (Specimens I, II and III) were prepared.

Comparative Example 2

Comparative Example 2 was performed as in Example 1 with the exceptions that unactivated kaolin of 50 g was employed instead of the activated kaolin of 50 g. Three specimens (Specimens I, II and III) were prepared.

Measurement of Physical Properties

Flexural strength, compressive strength and water permeability were measured for the specimens of Example 1 and Comparative Examples 1 and 2.

(1) Flexural Strength

Flexural strengths were measured according to Korean Industrial Standard KS L 5105. The distance of points was 100 mm and the applied force was 5 kg·force per second. The strengths of the specimens were shown in Table 6.

TABLE 6 unit: kg/cm² Specimens 1 2 3 average Example 1 85.6 89.1 86.6 87.1 Comparative Example 1 75.8 76.4 75.3 75.8 Comparative Example 2 55.4 53.1 56.7 55.1

As shown in Table 6, the mortar according to the present invention (Example 1) has an increase of 14.9% of the conventional mortar (Comparative Example 1) in flexural strength. The mortar using unactivated kaolin (Comparative Example 2) shows a decrease of 27.3% of the conventional mortar (Comparative Example 1) in flexural strength.

(2) Compressive Strength

Compressive strengths were measured according to KS L 5105. The applied force was 80 kg·force per second. After measurement of the flexural strength, six specimens per Example were tested. The compressive strengths of the specimens were shown in Table 7.

TABLE 7 unit: kg/cm² Specimens 1 2 3 4 5 6 average Example 1 952 958 934 923 942 933 947 Comp. Example 1 786 780 756 751 720 725 753 Comp. Example 2 682 690 702 710 623 629 686

As shown in Table 7, the mortar according to the present invention (Example 1) has an increase of 25.8% of the conventional mortar (Comparative Example 1) in compressive strength. The mortar using unactivated kaolin (Comparative Example 2) shows a decrease of 8.9% of the conventional mortar (Comparative Example 1) in compressive strength.

(3) Test of Water Permeability

In this test of water permeability, a sodium chloride solution was used for measuring the permeation area where chlorine ions permeated. The test was performed in accordance with a test method of Japanese Concrete Institute (JCI). Specimens of 40×40×160 mm were immersed in a 2.5% sodium chloride solution at 20° C. for 7 days. The specimens were dissected into two pieces. On the dissected surfaces, 0.1% sodium fluorinate solution and 0.1 N silver nitrate solution were sprayed. The fluorescent parts on the dissected surface are deemed as permeation area. FIG. 4 is a cross-sectional view of a specimen of mortar for testing water permeability thereof. The upper and bottom surfaces of specimens were coated with an epoxy resin not so as to permeate chlorineions. Thus, chlorine ions permeate into the inner parts of the specimens through the side surfaces. The depths of the permeation area were measured at positions A through F. The depths of the permeation area at the positions were shown in Table 8.

TABLE 8 unit: mm Specimen I Specimen II Specimen III Average Example 1 A 10.2 9.3 8.9 9.8 10.2 9.4 9.5 B 9.4 10.7 8.6 C 8.5 8.5 8.5 D 8.1 10.1 9.3 E 10.0 9.9 10.7 F 9.6 10.7 9.1 Comparative A 13.3 14.5 15.3 15.0 13.9 14.9 14.8 Example 1 B 14.7 16.0 15.8 C 15.3 14.7 14.9 D 15.4 14.2 16.0 E 13.5 16.0 13.7 F 14.8 13.8 15.1 Comparative A 13.3 14.6 15.5 16.3 15.5 15.0 15.3 Example 2 B 14.8 16.1 13.6 C 15.9 17.4 15.0 D 15.4 15.2 16.4 E 13.5 16.5 16.0 F 14.7 17.1 13.5

As shown in Table 8, the mortar according to the present invention (Example 1) shows a decrease of 35.8% of the conventional mortar (Comparative Example 1) in depth of permeation area. The mortar using unactivated kaolin (Comparative Example 2) shows an increase of 3.4% of the conventional mortar (Comparative Example 1) in depth of permeation area. From the test of water permeability, the mortar or cement using the activated kaolin powder prepared in accordance with the present invention was effective to prevent impurities such as chlorine ions, due to excellent water permeability.

It is apparent from the above that many modifications and changes are possible without departing from the spirit and scope of the present invention. 

What is claimed is:
 1. A method of preparing an activated kaolin powder compound for mixing with cement, which comprises: heating natural kaolin to 480° C. for a time period up to one hour, wherein the natural kaolin is primarily composed of halloysite; calcinating the heated natural kaolin in the range of 800°-950° C. over at least 15 minutes; quenching the calcinated kaolin; and pulverizing the quenched activated kaolin to form powder having particle sizes of 2 μm or less.
 2. An activated kaolin powder compound for mixing with cement for preparing mortar or concrete, having particle sizes of 2 μm or less and a specific gravity of 1.5 to 3.0, which is prepared by heating natural kaolin to 480° C. for a time period up to one hour, calcinating the heated natural kaolin in the range of 800°-950° C. over at least 15 minutes, quenching the calcinated kaolin, and pulverizing the quenched activated kaolin to form powder, wherein the natural kaolin is primarily composed of halloysite.
 3. A method of preparing an activated kaolin powder compound for mixing with cement, which comprises: heating natural kaolin to 480° C. for a time period up to one hour; calcinating the heated natural kaolin in the range of 800°-950° C. over at least 15 minutes; quenching the calcinated kaolin; and pulverizing the quenched activated kaolin to form said powder compound. 